OK 48.08是適用于諸如海洋工程等苛刻應用的LMA焊條，其具有極佳的機械性能。含有約1% Ni的焊縫金屬在溫度低至-40°C條件下具有較高的沖擊強度。該焊條的藥皮為經(jīng)過抗氣孔和氫致裂紋優(yōu)化的1新一代LMA型號。OK 48.08已經(jīng)過CTOD測試。

Typical Tensile Properties

As welded
Elongation	Tensile Strength	Yield Strength	保護氣體
26 %	630 MPa	540 MPa	ISO
-	-	-	AWS

夏比V型缺口沖擊性能

As welded
Impact Value	Testing Temperature	保護氣體
115 J	-50 °C	ISO
90 J	-60 °C	ISO

焊縫金屬分析

Mn
Mn	Mo	C	Si	Ni	Cr
1.2 %	-	-	-	-	-
Mo
Mn	Mo	C	Si	Ni	Cr
-	0.001 %	-	-	-	-
C
Mn	Mo	C	Si	Ni	Cr
-	-	0.06 %	-	-	-
Si
Mn	Mo	C	Si	Ni	Cr
-	-	-	0.35 %	-	-
Ni
Mn	Mo	C	Si	Ni	Cr
-	-	-	-	0.95 %	-
Cr
Mn	Mo	C	Si	Ni	Cr
-	-	-	-	-	0.02 %

熔敷數(shù)據(jù)

Fusion time per electrode at 90% I max	kg weld metal/kg electrodes	Number of electrodes/kg weld metal	安培	熔敷率	電壓 V	直徑
42 sec	0.57 kg	135.1	55-80 A	0.60 kg/h	22 V	2.0 x 300 mm
41 sec	0.57 kg	88	75-110 A	1.0 kg/h	27 V	2.5 x 350 mm
66 sec	0.62 kg	42.3	110-150 A	1.30 kg/h	22 V	3.2 x 350 mm
85 sec	0.66 kg	30.0	110-150 A	1.40 kg/h	22 V	3.2 x 450 mm
90 sec	0.69 kg	20.3	150-200 A	2.00 kg/h	22 V	4.0 x 450 mm
85 sec	0.69 kg	14.0	190-275 A	3.00 kg/h	23 V	5.0 x 450 mm